{"id":109174,"date":"2025-08-30T02:57:00","date_gmt":"2025-08-30T00:57:00","guid":{"rendered":"https:\/\/www.sonnenseite.com\/?p=109174"},"modified":"2025-08-30T09:25:03","modified_gmt":"2025-08-30T07:25:03","slug":"aesthetic-and-efficient-facades-fraunhofer-fep-presents-advances-in-building-integrated-photovoltaics","status":"publish","type":"post","link":"https:\/\/www.sonnenseite.com\/en\/future\/aesthetic-and-efficient-facades-fraunhofer-fep-presents-advances-in-building-integrated-photovoltaics\/","title":{"rendered":"Aesthetic and efficient facades: Fraunhofer FEP presents advances in building-integrated photovoltaics"},"content":{"rendered":"\n

As part of the Design-PV project, Fraunhofer FEP has made significant progress in developing aesthetically appealing solutions for building-integrated photovoltaics. <\/p>\n\n\n\n

Technologies such as roll-to-roll nanoimprint lithography enable solar modules to be seamlessly integrated into building facades without compromising the design. Initial tests show that the modules are visually indistinguishable from conventional facade elements yet offer high energy efficiency.<\/p>\n\n\n\n

Photovoltaics are a key pillar in achieving the goal of climate neutrality by 2045. Building-integrated photovoltaics (BIPV) offer a way to use previously unused space for energy production. However, to increase the acceptance and spread of BIPV, PV modules must be cost-effective, durable, and visually appealing when integrated into the facade.<\/p>\n\n\n\n

This is precisely what the Design-PV project, funded by the German Federal Ministry for Economic Affairs and Energy, is working on. Together with five partners, Fraunhofer FEP is developing decorative films for facade elements that are finished using roll-to-roll nanoimprint lithography (NIL). The aim is to achieve a uniform design on metal facade elements and photovoltaic modules by applying the decorative films to these elements. At the halfway point of the project, several designs from project partner Surteco GmbH were applied by Institute for Solar Energy Research in Hamelin (ISFH) to PV-active and non-active facade elements and tested.<\/p>\n\n\n\n

\u201cTests carried out by project partner ISFH show that the PV modules with decorative finishes are visually indistinguishable from conventional facade elements and, depending on the finish, achieve up to 80% of the performance of uncovered comparison modules,\u201d says Dr. Steffen G\u00fcnther, project manager at Fraunhofer FEP. This represents a significant step forward, as aesthetic aspects are often seen as an obstacle to the acceptance of BIPV solution.<\/p>\n\n\n\n

A particular challenge in the project is the adhesive strength of the decorative films on the front glass of the PV modules and on the metal layer of the facade elements. In addition, the decorative coating must adhere reliably to the ETFE (ethylene tetrafluoroethylene) film substrate, which is already established in architecture due to its excellent weather resistance. However, since ETFE has low surface adhesion, the films must be specially treated before coating. Fraunhofer FEP has developed a plasma process for this purpose that roughens the interface layer of the ETFE film on a nanometer scale, thereby significantly improving the adhesion of the decorative layers.<\/p>\n\n\n\n

The next steps in the project include testing additional designs and colors, as well as comprehensive tests on the long-term stability and weather resistance of the developed solutions. Fraunhofer FEP and its project partners are confident that these advances will contribute to further increasing the acceptance of BIPV solutions in architecture.<\/p>\n\n\n\n

More about nanoimprint lithography (NIL)<\/strong>
NIL is used to fabricate surface topographies on polymer films with feature sizes ranging from a few 100\u00a0nanometers across a few micrometers to the millimeter range in a roll-to-roll process. This enables large-scale, continuous production of films. A structured master roller is pressed into a liquid coating, while the coating is simultaneously cured. Cross-linking the lacquer using electron beams allows for fast and efficient curing of the structures and offers the flexibility to integrate various pigments or particles into the lacquer. The process is carried out on a web width of up to 1250\u00a0mm and a process speed of several tens of meters per minute, thus guaranteeing high productivity.<\/p>\n\n\n

Source<\/h5>\r\n\n\n\n

Fraunhofer-Institut f\u00fcr Elektronenstrahl- und Plasmatechnik FEP 2025<\/a><\/p>\n\n\n\n